CuAl10Fe5Ni5 acc. to DIN EN 1982 (CC333G)
Material
Composition in %
Density around g/cm3
Mech. Properties
Tensile Strength Rm (Mpa)
Yield Point Rp 0.2 (Mpa)
Elongation A (%)
Brinell Hardness (HB)
CuAl10 Fe5Ni5-C
Cu 76,0-83,0 Al 8,5-10,5 Fe 4,0-5,5 Ni 4,0-6,0
7,6
Centrifugal Continuous
650
280
13
150
Characteristics:High loaded parts in terms of strength and corrosion resistance. Resistant to cold and warm seawater. Very good weldable and therefore also suitable for mixed constructions.
Use:Mechanically and chemically stressed parts in mechanical engineering. Bearings in industrial furnaces. Components for food processing machinery. Material for non-sparkling tools. Highly stressed bearings and worm gears.
Remark:Moderate to severe machinability. Due to the poor emergency running properties CuAl10Fe5Ni5-C should only be used with proper lubrication.
Comparable specification:C95800
CuAl11Fe6Ni6 acc. to DIN EN 1982 (CC334G)
Material
Composition in %
Density around g/cm3
Mech. Properties
Tensile Strength Rm (Mpa)
Yield Point Rp 0.2 (Mpa)
Elongation A (%)
Brinell Hardness (HB)
CuAl11Fe6 Ni6-C
Cu 72,0-82,5 Al 10,0-12,0 Fe 4,0-7,0 Ni 4,0-7,5
7,6
Centrifugal Casting
750
380
5
185
Characteristics:Comparable to CuAl10Fe5Ni5, but with higher expectations on the cavitation and / or wear resistance.
Use:This material is suitable for mechanical and chemical stressed parts in the mechanical industry. Bearings in industrial furnaces. Components for food processing machinery. Material for non-sparkling tools. Highly stressed bearings and worm gears.
Remark:Moderate to severe machinability. Due to the poor emergency running properties CuAl11Fe6Ni6-C should only be used with proper lubrication.
CuAl10Ni5Fe4 acc. to DIN EN 12163/12165 (CW307G)
Material
Composition in %
Density around g/cm3
Mech. Properties
Tensile Strength Rm (Mpa)
Yield Point Rp 0.2 (Mpa)
Elongation A (%)
Brinell Hardness (HB)
CuAl10 Ni5Fe4
Cu Rest Al 8,5-11,0 Fe 3,0-5,0 Ni 4,0-6,0
7,6
drawn (R740S) pressed, M
740
400
8
Characteristics:High stability even at high temperatures, good corrosion resistance. Good resistance against scaling, erosion and cavitation. Resistant to neutral, acidic, watery mediums and sea-water. Good hot working properties.
Use:High-strength, wear resistant parts in the engine and gear construction. Screws, bolts and nuts, shafts, worm wheels and gears.
Remark:Moderate machinability.
Comparable specification:C63200
CuSn8 or CuSn8P acc. to DIN EN 12163/12165
Material
Composition in %
Density around g/cm3
Mech. Properties
Tensile Strength Rm (Mpa)
Yield Point Rp 0.2 (Mpa)
Elongation A (%)
Brinell Hardness (HB)
CW453K CW459K
P 0,01-0,4 (453K) P 0,2-0,4 (459K) Sn 7,5-8,5 Cu Rest
8,8
drawn, M pressed, M
Characteristics:Very good corrosion resistance and high strength properties. Very good sliding properties and wear resistance.
Use:Highly-stressed sliding elements (especially thin-walled bearings), sliding guides. Highly stressed worm gears and gear wheels, bolts and screws.
Remark:Moderate to severe machinability depending on the state of resistance.
Comparable specification:C52100
Download catalogue

Search contact person

You would like to order or have questions about our products?
Our sales team is at your disposal, whether by phone or e-mail.
Enter your postcode (germany) and find your personal contact.

Wenn Sie Google Maps nutzen wollen, müssen Sie in die Nutzung von Scripten, die von Google Servern bezogen werden, einwilligen. Geben Sie dazu Ihre Zustimmung über den Cookie-Banner dieser Website.
Ihr Ansprechpartner für Mittelrheinische Metallgießerei H. Beyer GmbH & Co. KG Telefon: Fax: E-Mail: zum Kontaktformular
Download our product catalogue